PolyOne Lubri-Tech™ AT-000/5T Black Acetal-Copolymer, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-000/5T Black Acetal-Copolymer, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Preliminary DataDescription/Features:PTFE LubricatedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.435 g/cc | 1.435 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.025 cm/cm | 0.015 - 0.025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.24 GPa | 325 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.900 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 216 °C | 380 - 420 °F | Molding |
| Mold Temperature | 60.0 - 71.1 °C | 140 - 160 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 hour | 2 hour |
Users viewing this material also viewed the following:
- Osprey Metals 304L/MA Master Alloy Stainless Steel Powder (Grade 90% - 22)
- PTS Trilac® ABS-HH2350 High Heat ABS
- LyondellBasell Plexar® PX3060 Extrudable Tie-Layer Resin - Anhydride Modified LLDPE
- Fiberfil® J-61/30/FR Polypropylene Copolymer, 30% Glass Reinforced, Flame Retardant
- Techmer ES HiFill® PA6/6 0190 Nylon 66
- American Elements Calcium Phosphate Nanoparticles
- ExxonMobil Bicor™ 30MB400 OPP Film
- Colorite Polymers Self Frosting™ 7511SF Vinyl Compound
- Buckeye Polymers BP ABS 6239 ABS
- Bulk Molding Compounds BMC A50-EG Low Glass, Encapsulation Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved