PolyOne Geon™ Vinyl Rigid Extrusion L1101 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L1101 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.59 GPa | 376 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 78.2 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 12.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
22.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 13.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
24.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| 13.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
24.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 53.8 J/cm @Temperature 23.0 °C |
0.101 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 156 J/cm @Temperature 23.0 °C |
0.292 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Colors Available | |
| Ease of Sizing | Excellent | |
| Features | Good Dimensional Stability | |
| Good Melt Strength | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 16343 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Profiles |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ HS404 High Performance Polypropylene Nanocomposite
- Poco Graphite AXF-5Q10W Biomedical Grade Graphite
- NOVA Chemicals Novapol® LF-0222-A LDPE Wire and Cable Resin (discontinued **)
- Ineos ABS Triax® 1120 ABS + Polyamide Blend (DAM)
- Lanxess Durethan® BKV 30 G H2.0 900051 Nylon 6, 30% Glass Fiber
- Schott N-LASF44 Glass
- Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- Toyobo Vylopet® EMC405A PET/PBT Blend
- Dow DOWLEX™ 2038 Linear Low Density Polyethylene
- DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 75 Gauge
Copyright © lookpolymers.com All Rights Reserved