PolyOne Geon™ Vinyl Rigid Extrusion 87560 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87560 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 51.8 MPa | 7510 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.73 GPa | 396 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.92 GPa | 424 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 0.750 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.41 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| 0.850 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.59 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| Dart Drop Total Energy | 60.1 J/cm @Temperature 23.0 °C |
0.113 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 199 J/cm @Temperature 23.0 °C |
0.373 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C @Thickness 3.18 mm |
149 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 191 - 204 °C | 376 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Sheet Extrusion | |
| PVC Cell Classification | 12443 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S50T Silicone Rubber
- Nilit FRIANYL B63 TF30 Nylon 6 for injection molding, 30% PTFE lubricated
- Abatron AboCast 8-20/Abocure 8-20 Epoxy (discontinued **)
- LG Chemical SEETEC PB283 HDPE
- Schott Glass 8360 Lead-Free Soft Glass
- Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion
- Teknor Apex APEX® 3611-95 Polyvinyl Chloride, Flexible
- ChevronTexaco Starplex® Moly NLGI Grade 1
- DAK Americas Laser+® B90B PET
- ExxonMobil Label-Lyte™ 52LLC210 Preliminary Data Sheet OPP Film
Copyright © lookpolymers.com All Rights Reserved