PolyOne Geon™ Vinyl Rigid Extrusion 87350 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87350 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 43.4 MPa | 6290 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 70.3 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 6.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
11.8 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| 7.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
13.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| 8.80 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
16.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 65.4 J/cm @Temperature 23.0 °C |
0.123 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 130 J/cm @Temperature 23.0 °C |
0.244 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.0 µm/m-°C | 40.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C @Thickness 3.18 mm |
154 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.899 mm |
V-0 @Thickness 0.0354 in |
ALL; UL 94 |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 204 °C | 370 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | General Purpose | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Sheet Extrusion | |
| PVC Cell Classification | 1-41332-23 | ASTM D4216 |
| 15343 | ASTM D1784 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Outdoor Applications |
Users viewing this material also viewed the following:
- Orion Engineered Carbons PUREX® HS 25 Carbon Black
- SABIC Innovative Plastics Lexan® EXL6414 PC
- Greene Tweed Avalon® 9 PTFE, Graphite Filled
- SolVin 382NG Polyvinyl Chloride Homopolymer
- Teknor Apex Telcar® TL-8732 Thermoplastic Elastomer
- Fainplast Compounds GS 7503 Flexible PVC, Injection Molding for Footwear
- Braskem CP 741 Blow Molding Polypropylene
- Arlon T2040-B004 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber
- Arkema Group KYNAR® 720, 720 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding and Extrusion
Copyright © lookpolymers.com All Rights Reserved