- PolyOne Geon™ Vinyl Flexible A9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
PolyOne Geon™ Vinyl Flexible A9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Flexible A9000 Polyvinyl Chloride, Flexible (PVC, Flexible).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recommended for interior applications.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.013 - 0.017 cm/cm | 0.013 - 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | 15 sec; ASTM D2240 |
| 90 | 90 | ASTM D2240 | |
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 510 mm/min; ASTM D638 |
| Tensile Strength | 10.9 MPa @Strain 100 % |
1580 psi @Strain 100 % |
510 mm/min; ASTM D638 |
| Elongation at Break | 390 % | 390 % | 510 mm/min; ASTM D638 |
| Tear Strength | 85.8 kN/m | 490 pli | Die C, 510 mm/min; ASTM D624 |
| Compression Set | 37 % @Temperature 23.0 °C, Time 79200 sec |
37 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 |
| Clash Berg Modulus | 0.545 GPa | 79.0 ksi | ASTM D1043 |
| 0.310 GPa @Temperature -24.0 °C |
45.0 ksi @Temperature -11.2 °F |
ASTM D1043 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -33.9 °C | -29.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % @Thickness 1.91 mm |
5.0 % @Thickness 0.0750 in |
ASTM D1003 |
| Transmission, Visible | 80 % @Thickness 1.91 mm |
80 % @Thickness 0.0750 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 177 - 182 °C | 351 - 360 °F | |
| 193 - 204 °C | 379 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | NSF 51 | Trans 9000 and Trans 9400. Max. Temperature of use = 100 degrees F. |
| Appearance | Clear/Transparent | |
| Features | General Purpose | |
| High Gloss | ||
| Forms | Pellets | |
| Generic Material | PVC, Flexible | |
| Generic Name | Polyvinyl Chloride, Flexible (PVC, Flexible) | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Film | |
| General Purpose | ||
| Hose | ||
| Sheet | ||
| Tubing |
Users viewing this material also viewed the following:
- Specialty Materials 5521 Boron Epoxy Prepreg Tape
- Saint-Gobain CHR® M815 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics LNP STAT-KON KE002 ACETAL
- A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene
- Trelleborg R396 Commercial Natural Rubber Polyisoprene
- Lubrizol Estane® 58201 Thermoplastic Polyurethane
- Epoxyset Epoxiohm EO-38M-3 Electrically Conductive Epoxy Adhesive
- Asahi Glass Fluon® PA7115 15% Polyimide, PTFE Filled Compound
- LNP ULTEM® SMU5834 Polyetherimide, 20% Carbon Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved