PolyOne Edgetek® PI-30GF/000R BLACK Polyether Imide (PEI)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	PolyOne Corporation
Trade Name	Edgetek®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Edgetek® PI-30GF/000R BLACK Polyether Imide (PEI).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.50 g/cc	1.50 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.18 mm	0.0010 - 0.0030 in/in @Thickness 0.125 in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 - 0.0090 cm/cm @Thickness 3.18 mm	0.0080 - 0.0090 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	157 MPa	22800 psi	5.1 mm/min; ASTM D638
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %	ASTM D638
Tensile Modulus	9.96 GPa	1440 ksi	5.1 mm/min; ASTM D638
Flexural Strength	221 MPa	32100 psi	1.3 mm/min; ASTM D790
Flexural Modulus	8.96 GPa	1300 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	0.640 J/cm	1.20 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	201 °C @Thickness 3.18 mm	394 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94

Descriptive Properties	Value	Comments
Features	Amorphous
	Good Chemical Resistance
	Good Dimensional Stability
	High Heat Resistance
	High Rigidity
Filler / Reinforcement	Glass Fiber Reinforcement, 30% Filler by Weight
Forms	Pellets
Generic Material	PEI
Generic Name	Polyether Imide (PEI)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Aerospace Applications
	Aircraft Applications
	Automotive Applications
	High Temperature Applications
	Industrial Applications