- Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
- Cossa Polimeri ESTASAN SAN 0840 GF Styrene Acrylonitrile
Cossa Polimeri ESTASAN SAN 0840 GF Styrene Acrylonitrile
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTASAN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTASAN SAN 0840 GF Styrene Acrylonitrile.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAN with 20% glass fiber reinforcementExcellent dimensional stability, good heat resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D 955 |
| Melt Flow | 12 g/10 min @Load 10.0 kg, Temperature 220 °C |
12 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D 638 |
| Elongation at Break | 1.4 % | 1.4 % | ASTM D 638 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.250 J/cm @Temperature 0.000 °C |
0.468 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 0.300 J/cm @Temperature 23.0 °C |
0.562 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 103 °C @Load 5.00 kg |
217 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 107 °C @Load 0.999 kg |
225 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 953 PC (Asia Pacific)
- Materion Beryllium Copper Alloy 25 Wire; AT (TF00) Temper; 1.3-12.7 mm Diameter (UNS C17200)
- Gwent Electronic Materials C2061027P13 High Brightness Phosphor Ink (Blue/Green)
- Haveg Havaflex T.A.-118 Phenolic, Trowelable Ablative Coating
- Lucas-Milhaupt Silvaloy® 50 Brazing Alloy
- Taiwan PU Corporation TPU-E80 General Grade, Extrusion Molding Polyester Base TPU
- Teknor Apex Fireguard® 910-A10-NL2 Polyvinyl Chloride, Flexible
- Hexcel® HexPly® 1458 160°C-180°C Curing Epoxy Matrix
- Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
Copyright © lookpolymers.com All Rights Reserved