PolyOne Edgetek® NI-20GF/000 Nylon 6/10, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NI-20GF/000 Nylon 6/10, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 121 MPa | 17500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Shear Strength | 65.5 MPa | 9500 psi | ASTM D732 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.2 µm/m-°C @Temperature 20.0 °C |
24.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 °C | 540 °F | Molding |
| Mold Temperature | >= 93.3 °C | >= 200 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPS7R PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® FXD163R PC (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 19-7744 Polyamide 46, with aramid reinforcement and PTFE
- Gromax Melamine (Fine Grade)
- SABIC Innovative Plastics LNP Thermocomp RX06027 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL APS430 PPE+PPS (Asia Pacific)
- Universal Wire Works BNi-5 (AMS 4782) Nickel Base Brazing Filler Metal
- A. Schulman POLYBATCH™ Teal 30316 Concentrate Based In LLDPE
- ExxonMobil Gargoyle Arctic 226 SHC 200 Series
- Abatron AboWeld 8104-13 Polysulfide-Epoxy Sealant and Caulk
Copyright © lookpolymers.com All Rights Reserved