- PolyOne Edgetek® ES-30GF/000 PES (Polyethersulfone), 30% Glass Reinforced, Hi-Temp (discontinued **)
PolyOne Edgetek® ES-30GF/000 PES (Polyethersulfone), 30% Glass Reinforced, Hi-Temp (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ES-30GF/000 PES (Polyethersulfone), 30% Glass Reinforced, Hi-Temp
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne™ Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Water Absorption | 0.35 % @Thickness 3.17 mm |
0.35 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 140 MPa | 20300 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 190 MPa | 27500 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | Method A, Injection Molded, 0.125 in bars, 73°F; ASTM D648 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 382 °C | 670 - 720 °F | Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Processing Method | Injection Molding |
Users viewing this material also viewed the following:
- LG Chemical Lupox® GP2100 PBT+GF10%
- LG Chemical Lupox® SV1120M PBT
- M Cubed Technologies SSC-802 Reaction-Bonded Silicon Carbide
- Topas Advanced Polymers TOPAS® 6013S-04 Cyclic Olefin Copolymer (COC)
- A. Schulman POLYBATCH™ Blue 4500 Concentrate Based In Polyethylene
- CMW® D55F Pre-oxidized Silver Cadmium Oxide Contact Material ASTM B781, Table 3
- Fainplast Compounds KL 90/4 Flexible PVC, Insulation for High Temperatures Lead Free
- 3M 3513 Copper Foil Tape
- MV Labs RH470 [(C6H5)3P]2Rh(CO)Cl Carbonylchlorobis(triphenylphosphine) rhodium(I)
- Zhejiang Juner PC/PBT Alloy
Copyright © lookpolymers.com All Rights Reserved