- PolyOne Edgetek® AT-10GF/000 FDA Acetal-Copolymer, Glass Filled (discontinued **)
PolyOne Edgetek® AT-10GF/000 FDA Acetal-Copolymer, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AT-10GF/000 FDA Acetal-Copolymer, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedFDA CapablePolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 227 °C | 400 - 440 °F | Molding |
| Mold Temperature | 54.4 - 71.1 °C | 130 - 160 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PolyChem Alloy PolyOxyter 2501
- Covestro Makrolon® 1239 Polycarbonate, Blow Molding/Extrusion Grade (discontinued **)
- Lord Adhesives 6144 Silver Conductor
- Minelco 47 Sarca Chamottes
- SABIC Innovative Plastics LNP LUBRICOMP KI001XXJ Acetal
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter
- Unifrax Fiberfrax® 6001-F-5 Kaolin Bulk Fiber
- ExxonMobil 68 Mobil EAL Arctic Series
- A. Schulman POLYBATCH™ Grey 8368 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved