- PolyOne Edgetek® AS-15GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
PolyOne Edgetek® AS-15GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-15GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion, -; ASTM D570 |
| 0.80 % | 0.80 % | Long-Term Immersion, -; ASTM D570 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.17 GPa | 750 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.30 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C | 205 °F | Annealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 243 °C | 430 - 470 °F | Molding |
| Mold Temperature | 37.8 - 82.2 °C | 100 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | 2 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- NEXA® PFX8045 Perfluoroelastomer
- Hardwire 3x2 Cord
- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
- Unitika TERRAMAC TE-8300 Polylactic Acid (PLA)
- Wanhua Chemical Wanthane® WHT-6420B TPU Solvent-Based Adhesive
- Loctite® 5420 Heat Cure Form-In-Place Electrically Conductive Silicone Sealant
- Dow Corning S40 LIQUID SILICONE RUBBER KIT
- DuPont™ Kapton® MT Polyimide Film
- Reliance Industries Polypropylene - 40% Glass filled
Copyright © lookpolymers.com All Rights Reserved