PolyOne Edgetek® AS-10CF/000 ABS - 10% Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-10CF/000 ABS - 10% Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0025 - 0.0035 cm/cm @Thickness 3.17 mm |
0.0025 - 0.0035 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 79.0 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 5.90 GPa | 856 ksi | ASTM D638 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 6.35 mm |
1.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 100 - 1000 ohm-cm | 100 - 1000 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | Stock |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Drying Temperature | 77.0 °C | 171 °F |
Users viewing this material also viewed the following:
- Nyco MD400 WOLLASTOCOAT® Wollastonite
- Rogers Corporation Poron® 4701-60-15 Cellular Urethane Foam
- Proto3000 Objet Digital Materials™ DM_9860/9760 Rubber-like Prototyping Polymer
- Pau Tai Unistab BT-18A Organotin Stabilizer Butyl/Octyl Carboxylate Tin
- Lubrizol Advanced Materials PEARLTHANE® 15N95UV Thermoplastic Polyurethane Elastomer
- Eagle Brass 151 ZHC® COPPER, 1/4 Hard
- Eastman Tenite 360E3V45512 Propionate Water Clear, Trsp
- Barlog Plastics KEBAFLEX S 65 A.02 TPE-S, Shore A65, translucent
- DSM Stanyl® TS271A1 PA46-RF
Copyright © lookpolymers.com All Rights Reserved