PolyOne Bergamid™ A700 G20 UF Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ A700 G20 UF Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ±0.03 g/cm³; DIN 53479 |
| Ash | 20 % | 20 % | ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
ISO 527-2/5 |
| Elongation at Break | 2.1 % @Temperature 23.0 °C |
2.1 % @Temperature 73.4 °F |
ISO 527-2/5 |
| Tensile Modulus | 8.50 GPa @Temperature 23.0 °C |
1230 ksi @Temperature 73.4 °F |
ISO 527-2/1 |
| Charpy Impact Unnotched | 9.90 J/cm² @Temperature 23.0 °C |
47.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ISO 3146 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| 220 °C | 428 °F | Short Time; IEC 60216 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
ALL; Internal Method |
| Glow Wire Test | 969 °C @Thickness 3.00 mm |
1780 °F @Thickness 0.118 in |
0.8 mm wire; Ignition Temperature; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Flame Retardant | |
| Halogen Free | ||
| Low (to None) Phosphorus Content | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 20% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Infiltrated High Carbon Steel FX-232-T Powdered Metal
- 1055D Polyurethane-based Biomedical Elastomer
- M. Holland Company LD500 LDPE (discontinued **)
- MetalTek MTEK 375 Aluminum Bronze
- Kingfa JH710 G30 Flame Retardant & 30% Glass Fiber Reinforced PC
- Diamond Polymers NPP10-2523 Low Density Polyethylene
- 3M 3105 (Clear) Polyethylene Protective Tapes
- ATI Wah Chang Infiltrated Tungsten (Copper)
- ACC QSil 40 QSI Quantum Silicones 40 Durometer Condensation Cure for Potting
- DuPont™ Kapton® 200VN Polyimide Film, 50 Micron Thickness
Copyright © lookpolymers.com All Rights Reserved