Polimeri Europa SINKRAL B532 ABS, Very High Impact (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa SINKRAL B532 ABS, Very High Impact
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very high impact; injection/extrusion grade.Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Cond. I; ASTM D1238 |
| 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Yield | 40.7 MPa | 5900 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Modulus | 2.21 GPa | 321 ksi | ASTM D790 |
| Izod Impact, Notched | 4.50 J/cm @Thickness 3.17 mm |
8.43 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | 1/8 inch |
| HB | HB | 1/16 inch |
Users viewing this material also viewed the following:
- PolyOne Edgetek® NJ-10GF/000 Nylon 12 - 10% Glass Fiber (discontinued **)
- Materion Beryllium Copper Alloy 10 Rod and Bar; H (TD04) Temper; up to 76 mm (UNS C17500)
- Industeel CREUSABRO® 4800 Advanced Technology in Wear Steel
- Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized
- LyondellBasell Pro-fax SR549M Polypropylene Random Copolymer, Clarified
- Teknor Apex Uniprene® UN-7010-40D-NT Thermoplastic Vulcanizate
- Formosa Plastics Formolene® 1102L Homopolymer Polypropylene
- 3M 520 Sandblast Stencil
- Austin Novel Materials Texalan® 472D Polyester-based TPU
Copyright © lookpolymers.com All Rights Reserved