Industrial Laminates/Norplex NP347 Cotton Fabric

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP347 Cotton Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150°C continuous operation.Thickness Tested: 0.062", 0.125" & 0.500".
Physical Properties Metric English Comments
Specific Gravity 1.35 - 1.45 g/cc

@Thickness 1.57 mm
 1.35 - 1.45 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 1.6 %

@Thickness 1.57 mm
 1.6 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 48.3 MPa

@Thickness 1.57 mm
 7000 psi

@Thickness 0.0620 in
 CW; ASTM D638
82.7 MPa

@Thickness 1.57 mm
 12000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 6.89 GPa

@Thickness 1.57 mm
 1000 ksi

@Thickness 0.0620 in
 CW; ASTM D229
10.3 GPa

@Thickness 1.57 mm
 1500 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 110 MPa

@Thickness 1.57 mm
 16000 psi

@Thickness 0.0620 in
 CW; ASTM D790
145 MPa

@Thickness 1.57 mm
 21000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 248 MPa

@Thickness 12.7 mm
 36000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 93.1 MPa

@Thickness 15.7 mm
 13500 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.961 J/cm

@Thickness 12.7 mm
 1.80 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
1.28 J/cm

@Thickness 12.7 mm
 2.40 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.78 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 16.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.89 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 150 °C
302 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Descriptive Properties Value Comments
Bond Strength 2200 lb
0.5", ASTM D229
Color Natural