- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- PlastxWorld CEVIAN®-V 450 ABS
PlastxWorld CEVIAN®-V 450 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | PlastxWorld, Inc. |
| Trade Name | CEVIAN®-V |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastxWorld CEVIAN®-V 450 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat Resistant ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM 638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 1.98 J/cm @Thickness 3.17 mm |
3.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.4 µm/m-°C @Temperature 20.0 °C |
43.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | 0.5 inch; ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- RheTech Products HP800-706UV 20% Talc Reinforced High Performance Polypropylene Copolymer, Scratch Resistant, UV Stabilized, Impact Modified, SWB White
- Lord Adhesives 8661 Polymer Resistor Composition
- Techmer ES Luriblend® PA6 ML2 Nylon 6
- TIMCAL TIMREX® KS5-44 Primary Synthetic Graphite
- Covestro Makroblend® S 7916/2 Polycarbonate + PBT, Impact Grade
- DuPont Performance Polymers Zytel® 70G20HSL NC010 Nylon 66
- Bapolene® 152B Polyethylene Film Grade
- Aleris Weldural Aluminum Alloy, 600 mm Thickness
- ALM D80-ST Nylon 11 SLS Prototyping Polymer
- Premix Premi-Glas® 7203-28 28% Glass Reinforced Polyester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved