Plastics Group Polifil® 628L Nylon 6/6 (DAM)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	The Plastics Group of America
Trade Name	Polifil®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastics Group Polifil® 628L Nylon 6/6 (DAM).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Polifil® NYLON 6/6 combines good abrasion and chemical resistance.Applications: ValvesBearingsBearing casesStandard processing techniques are applicable. Information provided by The Plastics Group.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ASTM D792
Water Absorption	1.5 %	1.5 %	24 hours; ASTM D570
Linear Mold Shrinkage	0.015 cm/cm @Thickness 3.17 mm	0.015 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM D785
Tensile Strength at Break	81.4 MPa	11800 psi	ASTM D638
Elongation at Break	50 %	50 %	ASTM D638
Elongation at Yield	5.0 %	5.0 %	ASTM D638
Flexural Strength	89.6 MPa	13000 psi	ASTM D790
Flexural Modulus	2.80 GPa	406 ksi	Tangent; ASTM D790
Izod Impact, Notched	0.534 J/cm	1.00 ft-lb/in	At 73°F; ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	255 °C	491 °F	ASTM D789
Deflection Temperature at 0.46 MPa (66 psi)	235 °C	455 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C	194 °F	ASTM D648

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	25.2 kV/mm	640 kV/in	ASTM D149