Chevron Phillips 7109DT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chevron Phillips 7109DT LLDPE Blown Film Resin, Hexene Copolymer
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Resin Type: Hexene Copolymer, No Slip, No Antiblock Version of 7109T with Process Aid, Cast/Blown Film ResinCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPEApplications:Industrial Liners, Garment Bags, Carrier Bags, CoextrusionsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.1905 cm. Blow-Up Ratio 2:1.Film properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 |
| Secant Modulus, MD | 0.250 GPa | 36.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.310 GPa | 45.0 ksi | ASTM D882 |
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 16.5 g/micron | 420 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.1 g/micron | 840 g/mil | ASTM D1922 |
| Dart Drop | 4.70 g/micron | 119 g/mil | F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 53.0 MPa | 7690 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 53.0 MPa | 7690 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % | 11 % | ASTM D2457 |
| Gloss | 60 % | 60 % | at 45°. ASTM D 2457 |
| 100 % | 100 % | at 60°. ASTM D 2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 °C | 428 °F |
Users viewing this material also viewed the following:
- Oxford Polymers 10GF 10% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
- Saint-Gobain Rulon® E Grade Bearing/Seal PTFE (discontinued **)
- Lubriplate Wheel Bearing Grease Automotive Lubricant
- Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire
- Spartech Polycast Poly 900 (DTD-5592-UK) Cell Cast Acrylic
- SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT (Asia Pacific)
- Trelleborg T528 Butyl Rubber
- NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved