Plaskolite Optix® CP - 927 GHF High Impact Grade Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CP - 927 GHF High Impact Grade Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 12 g/10 min @Load 3.80 kg, Temperature 230 °C |
12 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 49.6 MPa | 7200 psi | ASTM D-638 |
| Elongation at Break | 5.3 % | 5.3 % | ASTM D-638 |
| Modulus of Elasticity | 2.38 GPa | 345 ksi | ASTM D-638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D-790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm |
0.900 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 3.16 J @Thickness 3.17 mm |
2.33 ft-lb @Thickness 0.125 in |
Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ASTM D-696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.3 °C | 164 °F | ASTM D-648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D-1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 2.0 % | <= 2.0 % | ASTM D-1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D-1003 |
Users viewing this material also viewed the following:
- MV Labs HO810 Ho2O3 Holmium oxide
- Precision Polymer Engineering N90K Nitrile Rubber
- Abatron 2231 A/B Filled Potting Compound (discontinued **)
- Fibre Glast 543 Style 7781 E-Glass Fiberglass Fabric
- Lord Adhesives 7545F Two-Component, Equal-Mix, Non-Sag Urethane Adhesive
- SABIC Innovative Plastics Ultem MD131A PEI (Europe-Africa-Middle East)
- EMS-Grivory Grivory® TSG-30/4 H black 9836 PA666-GF30
- ArcelorMittal MartINsite® 1500 Cold Rolled Steel
- Quantum Composites QC-8151C 55% Glass Fiber Vinyl Ester Static-Dissipative SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved