Plaskolite Optix® CA - 2000 High Impact Grade Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CA - 2000 High Impact Grade Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 38.6 MPa | 5600 psi | ASTM D-638 |
| Elongation at Break | 40 % | 40 % | ASTM D-638 |
| Modulus of Elasticity | 1.86 GPa | 270 ksi | ASTM D-638 |
| Flexural Strength | 66.2 MPa | 9600 psi | ASTM D-790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm |
2.00 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 9.04 J @Thickness 3.17 mm |
6.67 ft-lb @Thickness 0.125 in |
Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ASTM D-696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D-648 |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D-1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.0 % | <= 3.0 % | ASTM D-1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D-1003 |
Users viewing this material also viewed the following:
- Teknor Apex Flexalloy® 9900-40 Polyvinyl Chloride Elastomer
- Master Bond EP30P Epoxy Bonds Glass, Polycarbonates and Acrylics
- A. Schulman PP 2407 Polypropylene Impact Resistant Copolymer Polypropylene
- ExxonMobil Label-Lyte™ 29LL210 Preliminary Data Sheet OPP Film
- DuPont Teijin Films Mylar® C Polyester Film, 14 Gauge
- 3M Dyneon™ FC 2122 Fluoroelastomer
- Resinlab® RC8003 Anaerobic Retaining Compound
- DuPont Performance Polymers Neoprene 571 Polychloroprene (discontinued **)
- SABIC Innovative Plastics GELOY CR7500 ASA
Copyright © lookpolymers.com All Rights Reserved