- PolyOne Lubri-Tech™ MP-20GF/15T Modified PPO - 20% Glass Fiber - 15% PTFE (discontinued **)
PolyOne Lubri-Tech™ MP-20GF/15T Modified PPO - 20% Glass Fiber - 15% PTFE (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ MP-20GF/15T Modified PPO - 20% Glass Fiber - 15% PTFE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 79.0 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 1.0 - 5.0 % | 1.0 - 5.0 % | ASTM D638 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 - 1.17 J/cm @Thickness 6.35 mm |
1.70 - 2.19 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 293 - 327 °C | 559 - 621 °F | Stock |
| Mold Temperature | 93.0 °C | 199 °F | |
| Drying Temperature | 93.0 °C | 199 °F |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ U 5380A-S0013 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics LNP COLORCOMP D10006U PC
- Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK) (Unverified Data**)
- Palm Labs Adhesives TURBO-LOCK SERIES 17-GP Anaerobic Thread Locking Compound
- Honeywell Aegisâ„¢ H100MP Nylon 6 Extrusion Grade Homopolymer Film
- LG Chemical LUMID SG2600B PA6+GF60%, General purpose, Good Surface
- Dow Corning HV 1760/65 Silicone Rubber
- ExxonMobil Mobil Zerice 68 S Oil
- Styrolution Luran® 348 Q Transparent SAN
Copyright © lookpolymers.com All Rights Reserved