Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K 2x2 Twill Reinforced

Category	Polymer , Thermoset , Epoxy
Manufacturer	Park Electrochemical Corp.
Trade Name	Nelcote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K 2x2 Twill Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request.Key Features and Benefits:Designed to replace first generation 350°F (176°C) cure systems.Wide cure temperature process window of 250°F to 350°FExhibits very low void content, i.e.,

Physical Properties	Metric	English	Comments
Volatiles	<= 1.5 %	<= 1.5 %
Thickness	381 microns	15.0 mil	cured, per ply

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	841 MPa @Temperature 21.1 °C	122000 psi @Temperature 70.0 °F	0° Direction, Dry; Vacuum/Oven Cured; ASTM D3039-95
Tensile Modulus	57.9 GPa @Temperature 21.1 °C	8400 ksi @Temperature 70.0 °F	0° Direction, Dry; Vacuum/Oven Cured; ASTM D3039-95
Compressive Strength	738 MPa @Temperature 21.1 °C	107000 psi @Temperature 70.0 °F	Dry; Vacuum/Oven Cured; SACMA 1-94
Compressive Modulus	55.8 GPa @Temperature 21.1 °C	8100 ksi @Temperature 70.0 °F	Dry; Vacuum/Oven Cured; SACMA 1-94
Shear Strength	60.7 MPa @Temperature 21.1 °C	8800 psi @Temperature 70.0 °F	Short-Beam, Dry; Vacuum/Oven Cured; ASTM D2344

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	165 °C	329 °F	Dry; DMA

Processing Properties	Metric	English	Comments
Gel Time	2.00 - 6.00 min @Temperature 135 °C	2.00 - 6.00 min @Temperature 275 °F
Shelf Life	6.00 Month @Temperature -17.8 °C	6.00 Month @Temperature 0.000 °F

Descriptive Properties	Value	Comments
Fabric Area Weight (g/m²)	370
Prepreg Resin Content (%)	37-43
Resin Flow (%)	12-24	275°F, 15psi
Tack	Light-Medium