Samsung Cheil Industries Starex® WR-9750H ASA, Unreinforced Extrusion Grade
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9750H ASA, Unreinforced Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 91 | 91 | ASTM D785 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 75 % | 75 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 52.0 MPa | 7540 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.67 GPa | 242 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 4.90 J/cm @Thickness 3.17 mm |
9.18 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-(VE) 12 MFI UV Stabilized Polycarbonate With Release
- LyondellBasell Aquathene® FR409800 Polyethylene Wire and Cable Compound
- Ferro EG 2778 Thick Film Glass
- LTL Color Compounds ColorRxâ„¢ PP1-2005ARX Biocompatible Polypropylene Homopolymer
- Lucite International Elvacite ® 2016 Acrylic Resin
- Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
- SABIC Innovative Plastics Valox® 4012G PBT (Europe-Africa-Middle East)
- SK Chemicals SKYTHANE® S375D Polyester Based Thermoplastic Polyurethane Elastomer
- Bohler-Uddeholm AISI D2 Cold Work Tool Steel
Copyright © lookpolymers.com All Rights Reserved