- SABIC Innovative Plastics Ultem PW2400 PEI (Europe-Africa-Middle East)
SABIC Innovative Plastics Ultem PW2400 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem PW2400 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass fiber filled, standard flow Polyetherimide (Tg 217°C). Product designed and certified for use in Potable Water
applications. KTW, WRAS, ACS certified. NSF61 and W270 pending. US FDA and European Food Contact approved.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.80 % @Temperature 23.0 °C |
0.80 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on tensile bar; SABIC Method |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 11.5 GPa | 1670 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Taber Abrasion, mg/1000 Cycles | 20 @Load 1.00 kg |
20 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 150 °C |
8.33 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 217 °C | 423 °F | Rate B/50; ISO 306 |
| 225 °C | 437 °F | Rate B/120; ISO 306 | |
| 230 °C | 446 °F | Rate A/50; ISO 306 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Oxygen Index | 48 % | 48 % | LOI; ISO 4589 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Kinetics MIM 4605 Low Alloy Steel (Quenched + Tempered)
- Karina 18/335-FC Gray Color Concentrate for PVC
- SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 (Asia Pacific)
- Chase Plastics CP Pryme® NN130GMD2 (DAM) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated
- DuPont™ Nomex® N196 Paper, 15 mil Nominal Thickness
- Arlon LW40125B12-P0 0.040" Self-Fusing Silicone Rubber Tape
- Teknor Apex Fireguard® 910-FOB-NL1 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved