PTS Tristar® PC-10FRNH-V 12 MFI Non-Bromine Non-Chlorine Flame Retardant UV Stabilized Polycarbonate With Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-10FRNH-V 12 MFI Non-Bromine Non-Chlorine Flame Retardant UV Stabilized Polycarbonate With Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hours at 73°F; ASTM D570 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 61.4 MPa @Thickness 3.17 mm |
8900 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 75 % @Thickness 3.17 mm |
75 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 96.5 MPa @Thickness 3.17 mm |
14000 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.34 GPa @Thickness 3.17 mm |
340 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 6.94 J/cm @Thickness 3.17 mm |
13.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
colors; E-155285 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 - 274 °C | 490 - 525 °F | |
| Middle Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Front Barrel Temperature | 277 - 293 °C | 530 - 560 °F | |
| Nozzle Temperature | 271 - 293 °C | 520 - 560 °F | |
| Melt Temperature | 282 - 304 °C | 540 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 75.8 - 124 MPa | 11000 - 18000 psi | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Edge Gate | Slow to Medium | |
| Tab Gate | Medium to Fast | |
| Tunnel Gate | Fast |
Users viewing this material also viewed the following:
- Nyco MD400 WOLLASTOCOAT® Wollastonite
- Murtfeldt Murylat® Polyethylene Terephthalate
- 3M Dyneon™ CC174/N Custom Fluoropolymer Compound (discontinued **)
- Momentive Performance Materials Siloprenâ„¢ LSR 3485/35 Liquid Silicone Rubber - Self-Lubricating / Standard
- Schott RG645 Long Pass Filter
- Samsung Cheil Industries Starex® VE-0856 (VE-0856U UV) Flame Retardant Grade ABS
- SABIC Innovative Plastics LNP THERMOCOMP VF008A PA 66
- Chase Plastics CP Pryme® N330GL (COND, 50% RH) Nylon 6 (Utility Grade), 30% Glass Fiber Reinforced, Internally Lubricated
- Zotefoams Evazote® VA35 Ethylene Vinyl Acetate Copolymer Foam
- Axiall 35551 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved