PTS PCA-30G11-(V) UV Stabilized, Glass Reinforced PC/PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS PCA-30G11-(V) UV Stabilized, Glass Reinforced PC/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 250 °C |
11 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa @Thickness 3.17 mm |
8990 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 6.0 % @Thickness 3.17 mm |
6.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 96.0 MPa @Thickness 3.17 mm |
13900 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.86 GPa @Thickness 3.17 mm |
415 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 2.13 J/cm @Thickness 3.17 mm |
3.99 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 257 - 279 °C | 495 - 535 °F | |
| Middle Barrel Temperature | 246 - 279 °C | 475 - 535 °F | |
| Front Barrel Temperature | 246 - 279 °C | 475 - 535 °F | |
| Nozzle Temperature | 246 - 279 °C | 475 - 535 °F | |
| Melt Temperature | 246 - 279 °C | 475 - 535 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 87.8 - 98.9 °C | 190 - 210 °F | 12 hours maximum |
| 98.9 °C | 210 °F | 4 hours minimum | |
| Dew Point | -40.0 °C | -40.0 °F | Preferred |
| <= -20.0 °C | <= -4.00 °F | ||
| Injection Pressure | 110 - 138 MPa | 16000 - 20000 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Shot Size | 50 - 70 % | 50 - 70 % | |
| Vent Depth | 0.00203 - 0.00254 cm | 0.000800 - 0.00100 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2243-24 CR-SX Fiberglass Reinforced Thermoset Thick Molding Compound
- PolyOne Geon™ 130 Series 136 Polyvinyl Chloride Copolymer (PVC Copolymer)
- ExxonMobil Escorene® LD-411 LDPE Power Cable Insulation (discontinued **)
- Kennametal Stellite Deloro® 38 Nickel Alloy
- Lubriplate Flush Pure USP Mineral Oil-Based Food Machinery Grade Oil
- Saint-Gobain Norton® Fluorglas® Chemfilm® DF2919 Fluoropolymer Tape
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 330ºF Cure Temperature
- A. Schulman POLYFORT™ FPP 1236-2939 Fiberglass Reinforced Homopolymer Polypropylene
- Asahi Kasei Thermofil P-40CC-0148 40% Calcium Carbonate Reinforced, Heat Stabilized
- LTL Color Compounds ColorFast® JCT1000 Polycarbonate-ABS-SMA Alloy
Copyright © lookpolymers.com All Rights Reserved