PTS PCA-30G00 Impact Modified Polycarbonate/PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | PTS PCA-30G00 Impact Modified Polycarbonate/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
For Cold Temperature Impact.Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % <br>@Time 86400 sec |
0.030 % <br>@Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0075 - 0.010 cm/cm | 0.0075 - 0.010 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min <br>@Load 3.80 kg,<br> Temperature 250 °C |
15 g/10 min <br>@Load 8.38 lb,<br> Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.0 MPa <br>@Thickness 3.17 mm |
7690 psi <br>@Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 115 % <br>@Thickness 3.17 mm |
115 % <br>@Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 82.0 MPa <br>@Thickness 3.17 mm |
11900 psi <br>@Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.00 GPa <br>@Thickness 3.17 mm |
290 ksi <br>@Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm <br>@Temperature -20.0 °C |
10.0 ft-lb/in <br>@Temperature -4.00 °F |
ASTM D256 |
| 8.01 J/cm <br>@Thickness 3.17 mm |
15.0 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB <br>@Thickness 1.50 mm |
HB <br>@Thickness 0.0591 in |
|
| HB <br>@Thickness 3.00 mm |
HB <br>@Thickness 0.118 in |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 T 25 TS PA6, 15% glass fibre, 25% mineral filling
- Ineos Nova S-5100 High Impact Compact Polystyrene (discontinued **)
- Pau Tai UNISTAB BZ-525 Liquid Barium-Zinc Stabilizer
- Lehmann & Voss LUVOCOM® 1200-7116-1 ABS, with carbon fiber
- SABIC Innovative Plastics LNP LUBRILOY ZX06315 PPE+SEBS+Polyolefin (Europe-Africa-Middle East)
- Tra-Con Tra-Bond 216E02 Encapsulant for "Fill" Applications
- Clariant Renol PA101F/ST801 Nylon 66, Impact Modified, Lubricated
- Fainplast Compounds CKL 80/3 Flexible PVC, Sheathing Lead Free
- 3M FM022R Indoor UL Recognized Clear Polyester Overlaminate Label Product
Copyright © lookpolymers.com All Rights Reserved