Oxford Polymers PP-Homopolymer-20GF-Natural PP, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer Oxford Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers PP-Homopolymer-20GF-Natural PP, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Glass Fiber (20% Reinforced), Polypropylene injection molding grade Processing and Delivery Form: Pellets and Injection Molding Special Characteristics: Improved stiffnessInformation provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D792
Water Absorption at Saturation 0.0300 %
0.0300 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00300 cm/cm

@Thickness 3.17 mm
0.00300 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.7 MPa
7500 psi
ASTM D638
Elongation at Break 3.00 %
3.00 %
ASTM D638
Flexural Strength 44.8 MPa
6500 psi
ASTM D790
Flexural Modulus 1.90 GPa
275 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.17 mm
1.10 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
265 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 227 °C
440 °F
Middle Barrel Temperature 238 °C
460 °F
Front Barrel Temperature 241 °C
465 °F
Nozzle Temperature 238 °C
460 °F
Melt Temperature 241 °C
465 °F
Mold Temperature 32.2 - 48.9 °C
90.0 - 120 °F
Drying Temperature 76.7 °C
170 °F
Dry Time 1.00 - 2.00 hour
1.00 - 2.00 hour