Master Bond FLM36 B-staged film for high performance bonding and sealing

Category	Polymer , Film , Thermoset , Epoxy , Epoxy, High Temperature
Manufacturer	Master Bond Inc.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Master Bond FLM36 B-staged film for high performance bonding and sealing.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Master Bond FLM36 is a film adhesive with exceptional strength properties, high temperature resistance and first class thermal conductivity and electrical insulation properties. Based on the Master Bond EP36AO formulation, this film differs from other heat resistant epoxies for it possesses far more toughness and flexibility than conventional high temperature resistant epoxies.High temperature resistantThermally conductiveTough and flexibleDoesn’t require freezing or refrigerationExcellent electrical insulation propertiesUniform bond line thickness

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	22 @Temperature 177 °C	22 @Temperature 350 °F
	27 @Temperature 100 °C	27 @Temperature 212 °F
	80 @Temperature 23.9 °C	80 @Temperature 75.0 °F
Tensile Strength	>= 13.8 MPa	>= 2000 psi
Elongation at Break	>= 50 %	>= 50 %
Adhesive Bond Strength	>= 27.6 MPa	>= 4000 psi	tensile lap shear, Al to Al

Thermal Properties	Metric	English
CTE, linear	70.0 - 82.0 µm/m-°C	38.9 - 45.6 µin/in-°F
Thermal Conductivity	1.30 - 1.44 W/m-K	9.00 - 10.0 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air	260 °C	500 °F
Minimum Service Temperature, Air	-73.3 °C	-100 °F
Glass Transition Temp, Tg	30.0 °C	86.0 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+14 ohm-cm	>= 1.00e+14 ohm-cm
Dielectric Constant	4.1 @Frequency 60.0 Hz	4.1 @Frequency 60.0 Hz

Processing Properties	Metric	English	Comments
Processing Temperature	177 °C @Time 3600 - 7200 sec	350 °F @Time 1.00 - 2.00 hour
Shelf Life	6.00 Month	6.00 Month	unopened containers at RT

Descriptive Properties	Value	Comments
Color	Black