Oxford Polymers PC 714-FR Series PC, Flame retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers PC 714-FR Series PC, Flame retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Amorphous, Polycarbonate injection molding grade, flame retardant Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents and UV stabilizersSpecial Characteristics: All colors Available and UL listed – VO @ 3mm File # E186411 conductiveInformation provided by Oxford Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.150 % | 0.150 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00500 - 0.00700 cm/cm @Thickness 3.17 mm |
0.00500 - 0.00700 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 9.00 - 14.0 g/10 min @Load 1.10 kg, Temperature 300 °C |
9.00 - 14.0 g/10 min @Load 2.43 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 5.00 % | 5.00 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.59 GPa | 375 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm @Thickness 3.17 mm |
16.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Middle Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Front Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Nozzle Temperature | 277 - 304 °C | 530 - 580 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | <= 121 °C | <= 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |