Oxford Polymers PC 46 Unfilled Polycarbonate for Blow and Extrusion Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Extruded |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers PC 46 Unfilled Polycarbonate for Blow and Extrusion Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled Polycarbonate for Blow and Extrusion MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 2.38 GPa | 345 ksi | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Compressive Strength | 86.2 MPa | 12500 psi | ASTM D695 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 288 °C | 550 °F |
Users viewing this material also viewed the following:
- Overview of materials for Polycarbonate/ABS Alloy, Unreinforced
- Techmer ES HiFill® PA6/6 GB20 L BK 20% Glass Bead Filler
- Unifrax Anchor-Loc®2 2600 Ceramic Fiber Modules
- Zotefoams Plastazote® HD115 High Density Polyethylene Foam
- DSM Akulon® K224-G0 Nylon 6-50% Glass Reinforced (European Grade) (Cond)
- DuPont™ Nomex® 410 Paper, 3 mil Nominal Thickness
- Arkema Group Orgalloy® LE 6006 Nylon Alloy, 6% Glass Fiber Reinforced (Conditioned)
- BASF Pluracol® GP 730 Specialty Polyol
- LNP Thermocomp® IF-1006 Polyamide 6/12 Copolymer, Glass Fiber Reinforcement (discontinued **)
- Osprey Metals 310S Stainless Steel Powder (Grade 90% - 16)
Copyright © lookpolymers.com All Rights Reserved