Oxford Polymers Oxtron PPS-XT-40GF PPS, 40% Glass Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer	Oxford Polymers
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Oxford Polymers Oxtron PPS-XT-40GF PPS, 40% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Glass Fiber (40% Reinforced), Polyphenylene sulfide injection molding grade based alloy. Processing and Delivery Form: Pellets and Injection MoldingAppearance: Natural off-white, brown or BlackInformation provided by Oxford Polymers

Physical Properties	Metric	English	Comments
Density	1.54 g/cc	0.0556 lb/in³	ASTM D792
Water Absorption at Saturation	0.0200 %	0.0200 %	ASTM D570
Linear Mold Shrinkage, Flow	0.00300 cm/cm @Thickness 3.17 mm	0.00300 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	159 MPa	23000 psi	ASTM D638
Elongation at Break	1.00 %	1.00 %	ASTM D638
Flexural Strength	221 MPa	32000 psi	ASTM D790
Flexural Modulus	12.4 GPa	1800 ksi	ASTM D790
Izod Impact, Notched	0.747 J/cm @Thickness 3.17 mm	1.40 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	241 °C	465 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	282 - 321 °C	540 - 610 °F
Mold Temperature	93.3 - 163 °C	200 - 325 °F
Drying Temperature	135 °C	275 °F
Dry Time	4.00 hour	4.00 hour