Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.045 g/cc | 0.03775 lb/in³ | ASTM D-792 |
Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D-955 |
Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 112 | 112 | ASTM D-785 |
Tensile Strength, Yield | 42.2 MPa @Thickness 3.20 mm |
6120 psi @Thickness 0.126 in |
Type 1, 5 mm/min; ASTM D-638 |
Flexural Yield Strength | 64.7 MPa @Thickness 6.40 mm |
9390 psi @Thickness 0.252 in |
ASTM D-790 |
Flexural Modulus | 2.16 GPa @Thickness 6.40 mm |
313 ksi @Thickness 0.252 in |
ASTM D-790 |
Izod Impact, Notched | 1.4706 J/cm @Thickness 6.40 mm |
2.7550 ft-lb/in @Thickness 0.252 in |
ASTM D-256 |
1.7647 J/cm @Thickness 3.20 mm |
3.3060 ft-lb/in @Thickness 0.126 in |
ASTM D-256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Method A - Annealed; ASTM D-648 |
Vicat Softening Point | 115 °C | 239 °F | Method B; ASTM D-1525 |
Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
UL-94 |