Overview of materials for PVC, Uncompounded

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Uncompounded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for PVC, Uncompounded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Uncompounded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.880 - 1.62 g/cc
0.0318 - 0.0585 lb/in³
Average value: 1.34 g/cc Grade Count:85
Apparent Bulk Density 0.470 - 0.620 g/cc
0.0170 - 0.0224 lb/in³
Average value: 0.551 g/cc Grade Count:9
Water Absorption 0.200 %
0.200 %
Average value: 0.200 % Grade Count:3
Particle Size 63.0 - 250 µm
63.0 - 250 µm
Average value: 157 µm Grade Count:8
Viscosity 1000 - 60000 cP
1000 - 60000 cP
Average value: 9750 cP Grade Count:12
Molecular Weight 60000 - 150000 g/mol
60000 - 150000 g/mol
Average value: 105000 g/mol Grade Count:19
Mechanical Properties Metric English Comments
Hardness, Shore A 50.0 - 98.0
50.0 - 98.0
Average value: 78.9 Grade Count:34
Hardness, Shore D 34.0 - 90.0
34.0 - 90.0
Average value: 59.7 Grade Count:18
Tensile Strength, Ultimate 8.48 - 80.0 MPa
1230 - 11600 psi
Average value: 16.6 MPa Grade Count:51
Tensile Strength, Yield 4.14 - 57.0 MPa
600 - 8270 psi
Average value: 19.9 MPa Grade Count:13
Elongation at Break 10.0 - 600 %
10.0 - 600 %
Average value: 298 % Grade Count:52
Elongation at Yield 3.00 - 4.00 %
3.00 - 4.00 %
Average value: 3.33 % Grade Count:3
Modulus of Elasticity 2.50 - 3.00 GPa
363 - 435 ksi
Average value: 2.75 GPa Grade Count:4
Charpy Impact, Notched 0.300 - 7.00 J/cm²
1.43 - 33.3 ft-lb/in²
Average value: 2.60 J/cm² Grade Count:3
Coefficient of Friction 0.600
0.600
Average value: 0.600 Grade Count:3
Tear Strength 40.0 - 75.0 kN/m
228 - 428 pli
Average value: 57.5 kN/m Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 60.0 - 80.0 µm/m-°C
33.3 - 44.4 µin/in-°F
Average value: 71.7 µm/m-°C Grade Count:3
Thermal Conductivity 0.120 - 0.140 W/m-K
0.833 - 0.972 BTU-in/hr-ft²-°F
Average value: 0.133 W/m-K Grade Count:3
Melting Point 160 - 302 °C
320 - 576 °F
Average value: 295 °C Grade Count:20
Maximum Service Temperature, Air 60.0 - 85.0 °C
140 - 185 °F
Average value: 66.3 °C Grade Count:4
Minimum Service Temperature, Air -15.0 - 0.000 °C
5.00 - 32.0 °F
Average value: -11.3 °C Grade Count:4
Brittleness Temperature -55.0 - -16.0 °C
-67.0 - 3.20 °F
Average value: -34.1 °C Grade Count:16
Flammability, UL94 V-0
V-0
Grade Count:5
Oxygen Index 25.0 - 55.0 %
25.0 - 55.0 %
Average value: 29.8 % Grade Count:22
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+16 ohm-cm
1000 - 1.00e+16 ohm-cm
Average value: 1.95e+15 ohm-cm Grade Count:11
Surface Resistance 1.00e+10 - 1.00e+16 ohm
1.00e+10 - 1.00e+16 ohm
Average value: 2.51e+15 ohm Grade Count:4
Dielectric Constant 2.30 - 3.80
2.30 - 3.80
Average value: 3.13 Grade Count:9
Dielectric Strength 20.0 - 50.0 kV/mm
508 - 1270 kV/in
Average value: 34.2 kV/mm Grade Count:3
Dissipation Factor 0.00590 - 0.278
0.00590 - 0.278
Average value: 0.104 Grade Count:3