Overview of materials for Glass Reinforced, Modified SMA

Category Polymer , Thermoplastic , SMA Polymer , Glass Reinforced, Modified SMA
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Glass Reinforced, Modified SMA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Glass Reinforced, Modified SMA". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.35 g/cc
0.0415 - 0.0488 lb/in³
Average value: 1.21 g/cc Grade Count:8
Filler Content 12.0 - 30.0 %
12.0 - 30.0 %
Average value: 17.4 % Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.00500 cm/cm
0.00100 - 0.00500 in/in
Average value: 0.00269 cm/cm Grade Count:8
Melt Flow 0.200 - 1.10 g/10 min
0.200 - 1.10 g/10 min
Average value: 0.660 g/10 min Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106 - 114
106 - 114
Average value: 111 Grade Count:3
Tensile Strength, Ultimate 55.0 - 103 MPa
7980 - 14900 psi
Average value: 71.5 MPa Grade Count:8
Elongation at Break 2.00 - 3.00 %
2.00 - 3.00 %
Average value: 2.67 % Grade Count:3
Elongation at Yield 1.70 - 2.40 %
1.70 - 2.40 %
Average value: 2.14 % Grade Count:5
Modulus of Elasticity 4.20 - 8.20 GPa
609 - 1190 ksi
Average value: 5.46 GPa Grade Count:5
Flexural Yield Strength 83.0 - 166 MPa
12000 - 24100 psi
Average value: 109 MPa Grade Count:8
Flexural Modulus 4.00 - 10.6 GPa
580 - 1540 ksi
Average value: 5.66 GPa Grade Count:8
Izod Impact, Notched 0.750 - 0.960 J/cm
1.41 - 1.80 ft-lb/in
Average value: 0.873 J/cm Grade Count:3
Izod Impact, Unnotched 2.67 - 3.84 J/cm
5.00 - 7.19 ft-lb/in
Average value: 3.10 J/cm Grade Count:3
Izod Impact, Notched (ISO) 7.80 - 11.4 kJ/m²
3.71 - 5.42 ft-lb/in²
Average value: 9.50 kJ/m² Grade Count:5
4.60 - 9.70 kJ/m²

@Temperature -40.0 - -40.0 °C
2.19 - 4.62 ft-lb/in²

@Temperature -40.0 - -40.0 °F
Average value: 6.98 kJ/m² Grade Count:5
Charpy Impact Unnotched 1.84 - 3.36 J/cm²
8.76 - 16.0 ft-lb/in²
Average value: 2.64 J/cm² Grade Count:5
Charpy Impact, Notched 0.770 - 1.38 J/cm²
3.66 - 6.57 ft-lb/in²
Average value: 1.05 J/cm² Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 43.2 - 59.4 µm/m-°C
24.0 - 33.0 µin/in-°F
Average value: 51.8 µm/m-°C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 120 - 132 °C
248 - 270 °F
Average value: 126 °C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 115 - 124 °C
239 - 255 °F
Average value: 120 °C Grade Count:8
Processing Properties Metric English Comments
Processing Temperature 227 - 288 °C
440 - 550 °F
Average value: 261 °C Grade Count:5
Melt Temperature 232 - 288 °C
450 - 550 °F
Average value: 262 °C Grade Count:8
Mold Temperature 32.2 - 71.1 °C
90.0 - 160 °F
Average value: 53.3 °C Grade Count:5