- Nilit RECONYL A SG30 Recycled nylon 6.6 for injection molding, 30% mineral filled
Nilit RECONYL A SG30 Recycled nylon 6.6 for injection molding, 30% mineral filled
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit RECONYL A SG30 Recycled nylon 6.6 for injection molding, 30% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled nylon 6.6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.4 % | 1.4 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.5 - 6.5 % | 5.5 - 6.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0080 - 0.017 cm/cm | 0.0080 - 0.017 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | ISO 527 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | DIN 53453 |
| 1.80 J/cm² @Temperature -40.0 °C |
8.57 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir RCL 600 Polystyrene (discontinued **)
- Chevron Phillips 2151 High Impact, Liner Grade Film Resin (discontinued **)
- Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA) (Unverified Data**)
- SABIC Innovative Plastics LNP LUBRICOMP RL003 PA 66 (Europe-Africa-Middle East)
- Loctite® 3564 Fast flow epoxy, moderate CTE and Tg Fast Flow Underfill
- Arkema Group Orevac® 9305 Film EVA-MAH Terpolymer
- Ascend Performance Materials Vydyne® 88X Nylon 66/6 Copolymer
- ATI Allegheny Ludlum 440A Martensitic Stainless Steel
- DuPont Performance Polymers Delrin® 100P NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved