Nilit FRIANYL B63 BR90 Nylon 6.6 for injection molding, 90% bronze filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 BR90 Nylon 6.6 for injection molding, 90% bronze filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.70 g/cc | 0.170 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 - 0.60 % | 0.30 - 0.60 % | ISO 62 |
| Water Absorption at Saturation | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 23 % | 23 % | ISO 527 |
| Tensile Modulus | 1.90 GPa | 276 ksi | ISO 527 |
| Flexural Strength | 37.0 MPa | 5370 psi | ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | DIN 53453 |
| 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 ohm-cm | 1.00e+8 ohm-cm | IEC 93 |
Users viewing this material also viewed the following:
- Nye Lubricants 793 (NG) Synthetic Oil
- Michelman® Hydrosize® U1-03 Phenoxy modified polyurethane dispersion
- Greene Tweed CHEMRAZ® 584 Perfluoroelastomer
- SABIC Innovative Plastics Valox® EH7020 PBT (Asia Pacific)
- DuPont Elvax® 40L-03 Ethylene-Vinyl Acetate Copolymer Resin
- Ensinger Tecapeek® XP-102 Compression Molded PEEK Compound, Filled with 15% Graphite and 10% PTFE
- Domo Domamid® 50 ABH Polyamide 6.6
- CLAL-MSX NICLAL 1300 0 Annealed Copper Alloy, Free Cutting Nickel-Silver
- Multibase Multibatch® MP 52518 BOPP White Pearlised Film
Copyright © lookpolymers.com All Rights Reserved