Schwartz Technical Plastics LAMIGAMID® 320 Cast Polyamide 6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 320 Cast Polyamide 6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: heavy-duty wheelsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | DIN 53473 |
| Water Absorption at Saturation | 7.0 % @Temperature 20.0 °C |
7.0 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 175 MPa | 25400 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO-DIS 527 |
| Creep Strength | >= 12.0 MPa | >= 1740 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 18.0 MPa | >= 2610 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 3.80 GPa | 551 ksi | DIN 53457 |
| Flexural Strength | 150 MPa | 21800 psi | DIN 54352 |
| Flexural Modulus | 3.70 GPa | 537 ksi | DIN 53457 |
| Compressive Strength | 56.0 MPa | 8120 psi | 5% pressing; EN ISO 604 |
| 79.0 MPa | 11500 psi | 10% pressing; EN ISO 604 | |
| 108 MPa | 15700 psi | 20% pressing; EN ISO 604 | |
| Izod Impact, Notched (ISO) | >= 2.50 kJ/m² | >= 1.19 ft-lb/in² | ISO 180-1A |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.040 | 0.040 | With lubrication |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.15 | >= 0.15 | ISO-DIS 527 |
| K Factor (Wear Factor) | 1.0e-10 | 1.0e-10 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 80.0 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 44.4 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |
| 180 °C | 356 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | V-notch; ISO R 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.030 | 0.030 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3c | DIN 53480 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM040LN Polypropylene, Impact Copolymer, Thermoforming
- Techno Polymer Techno ABS LM100 Transparent
- DSM Akulon® S223-PG6U (Cond.) 33% Glass Reinforced, Impact Modified Nylon 66 (North America) (discontinued **
- M. Holland Company CP501 Polypropylene Impact Copolymer
- Lehmann & Voss LUVOCOM® 1/CF/10/TF/20/GY Polyamide 66, with carbon fiber and PTFE, heat stabilized
- SABIC Innovative Plastics LNP Thermocomp MX88073 PP
- Chase Plastics CP Pryme® N100HL (Dry) Nylon 6, Heat Stabilized, Lubricated
- DuPont™ Selar® PA 3426R Nylon Barrier Resin
- Eurostar Starflam PZ00062E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
Copyright © lookpolymers.com All Rights Reserved