- Nilit FRIANYL A63 HS-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nilit FRIANYL A63 HS-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 HS-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.016 cm/cm | 0.0080 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 118 MPa | 17100 psi | ISO 2039-1 |
| Tensile Strength at Break | 109 MPa | 15800 psi | ISO 527 |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527 |
| Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527 |
| Flexural Strength | 123 MPa | 17800 psi | ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 3.60 J/cm² @Temperature -40.0 °C |
17.1 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.15 J/cm² | 5.47 ft-lb/in² | DIN 53453 |
| 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA | |
| 0.750 J/cm² @Temperature -40.0 °C |
3.57 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® LN 7000 Expandable Polystyrene
- Samsung Cheil Industries Starex® SG-301 Expandable Polystyrene (EPS) High Expansion
- Trelleborg Hypalon® H611 Chlorosulphonated Polyethylene
- CP-Polymer-Technik Wellamid® 6000 GX 350 HWCP Combination Nylon 6, Heat Stabilized, Conditioned
- DuPont Performance Polymers Zytel® HTN FR52G45BL BK337 Polyphthalamide (PPA) (Unverified Data**)
- CIMBAR BARIMITE™ 200 High Purity Barite (BaSO4)
- ConocoPhillips ANDEROL® 6100 Synthetic Food Grade Gear Fluid
- E-Polymers TEKAMID® TA210G33 , 33% Glass Fiber Reinforced PA66, DAM
- Bond Laminates TEPEX® dynalite 102-RGUD600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate
Copyright © lookpolymers.com All Rights Reserved