- Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced
Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.1 % | 1.4 - 2.1 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0040 - 0.014 cm/cm | 0.0040 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO 2039-1 |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | DIN 53453 |
| 2.70 J/cm² @Temperature -40.0 °C |
12.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| 0.420 J/cm² @Temperature -40.0 °C |
2.00 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 140 °C | 284 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyOne Gravi-Tech™ GRV-PS-027-BA-WHT Polybutylene Terephthalate (PBT)
- Permabond CSA-NF Cyanoacrylate Surface Activator
- Lehmann & Voss LUVOCOM® 50-7216 Polycarbonate, with PTFE, easy flowing
- M. Holland Company CP510 Polypropylene Copolymer
- Lavergne VYPET VNT 245 PET - PBT 45% Glass Reinforced Polyester
- Tisan TISAKRIL® 15% Glass Fiber Reinforced ABS
- ExxonMobil Label-Lyte™ 35LH247 OPP Film
- Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact
- Chang Chun Plastic PBT1100L General Purpose PBT
Copyright © lookpolymers.com All Rights Reserved