- Nilit FRIANYL A63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced
Nilit FRIANYL A63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding (good conductive and electrostatic properties).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 - 2.0 % | 1.3 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 7.0 % | 5.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 330 MPa | 47900 psi | ISO 2039-1 |
| Tensile Strength at Break | 237 MPa | 34400 psi | ISO 527 |
| Tensile Modulus | 21.0 GPa | 3050 ksi | ISO 527 |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | DIN 53453 |
| 2.70 J/cm² @Temperature -40.0 °C |
12.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 150 ohm-cm | 150 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
Users viewing this material also viewed the following:
- MV Labs FE1050 (NH4)2Fe(SO4)2·6H2O Ammonium iron(II) sulfate hexahydrate
- Plastcom SLOVAMID 66 T 40 Polyamide 66, 40% Mineral Filled
- Polymax® Maxelast® P3885M TPE, PP Overmold or Standalone use
- 3M Dyneon™ Fluorel™ FT-2320 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
- LNP ULTEM® SMU6303 Polyetherimide, 5% Glass Fiber Reinforcement, 5% PTFE Lubricant (discontinued **)
- Fibre Glast 1069 3K, 2x2 Twill Weave Carbon Fiber Fabric
- Sumitomo Bakelite Sumikon® PM-9640 Glass Filled Phenolic
- Total 1285 HDPE film
- ConocoPhillips Conoflex® 32 SRI Lubricant ISO
- ATI Allegheny Ludlum Type 316 Stainless Steel, UNS S31600
Copyright © lookpolymers.com All Rights Reserved