Nilit FRIANYL A63 CV-CM 0830 9005/Z Powder-coatable nylon 6.6 for injection molding, 8% carbon fiber reinforced, 30% ceramic filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 CV-CM 0830 9005/Z Powder-coatable nylon 6.6 for injection molding, 8% carbon fiber reinforced, 30% ceramic filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Powder-coatable nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.1 % | 1.4 - 2.1 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.021 cm/cm | 0.0080 - 0.021 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 185 MPa | 26800 psi | ISO 2039-1 |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eU |
| 1.50 J/cm² | 7.14 ft-lb/in² | DIN 53453 | |
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 1.40 J/cm² @Temperature -40.0 °C |
6.66 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| 0.400 J/cm² | 1.90 ft-lb/in² | DIN 53453 | |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| 0.300 J/cm² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Continuous; FRISETTA Test Method |
Users viewing this material also viewed the following:
- NYCOA 2326 HS Super-Tough, Heat Stabilized Nylon 6 Resin
- ExxonMobil Escorene® MV-02528 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- Resinlab® CYNERGY CA6603 Adhesive
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 12% Plasticizer (discontinued **)
- SABIC Innovative Plastics NORYL STN15HF PPE+PS
- Unipetrol PE HD LITEN® MB/ML 72 HDPE
- Total HL 428 HDPE Film Grade
- Dynasol Solprene® 412 Thermoplastic Elastomer
- Cheng Yu Plastic C1300 PC/ABS
Copyright © lookpolymers.com All Rights Reserved