ExxonMobil Bicor™ 18MB090 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 18MB090 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Biaxially oriented polypropylene film metallizable on one side, with a slip controlled broad seal range surface on the other side. Once metalized, film designed to be used in laminates as the inner web and is suitable for HFFS and VFFS applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent adhesion layer for metallizationBrilliant and homogeneous metal appearance after metallizationSlip controlled sealing layerExcellent processability in metallizationFor high barrier performance packagingOne side sealable, with broad sealing layer surfaceVery good hot tackHigh yieldFeatures:In Lamination Lap SealableApplications:IndustrialInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.51 g/m²/day @Temperature 23.0 °C |
0.0970 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 7.45 g/m²/day @Temperature 38.0 °C |
0.480 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 18.0 microns | 0.710 mil | ExxonMobil Method |
| Coating Weight | 16.2 g/m² | 10.1 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 175 % | 175 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 60 % | 60 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.60 GPa | 522 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.40 | 0.40 | Untreated; ExxonMobil Method |
| Seal Strength | 460 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
460 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Bruger, 0.2 sec; ExxonMobl Method |
| Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.5 % @Temperature 135 °C, Time 432 sec |
6.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 4.5 % @Temperature 135 °C, Time 432 sec |
4.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.6 % | 1.6 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 72°F | 36.3 psi, 0.2 sec |
| Yield | 43000 in2/lb |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® RN 50 U Linear Medium Density Polyethylene
- Okulen® 500 PE-HMW, Coloured
- Struktol POLYDIS 3610 Reactive, elastomer modified epoxy prepolymer (block-copolymer)
- Solvay RHODASURF® CET 2 Surfactant
- Tipco Tipcolite® TPF 1315 - Unreinforced Phenolic Resin having 22 mm Norton Flow with 10% Hexamine
- A. Schulman POLYTROPE™ TPP 1024E-01 Olefinic Elastomer For Sheet Extrusion
- Chosun Refractories HM-S Special Mortar for Sliding Gate Valve
- Braskem H 502 HC Injection Molding Polypropylene
- Alliance N-44H Neodymium Iron Boron Magnetic Material
- A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Copyright © lookpolymers.com All Rights Reserved