Network Polymers 779 Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers 779 Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Ignition RetardantInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 4.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 26.2 MPa | 3800 psi | ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | Injection Molding; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color Stability | min 3 | Change in E at 300 hours; ASTM D4459 |
Users viewing this material also viewed the following:
- Lanxess Durethan® CI 31 F 000000 Copolyamide PA6/6I
- Multibase Multi-Flex® TPE A 5002 BLK
- Saint-Gobain COHRlastic® 9235 High Performance Silicone Solid Rubber
- Teknor Apex APEX® 1519-39 Polyvinyl Chloride, Flexible
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- E-Polymers TEKAPPO® JF1 Un-Reinforced Flame Retardant M-PPO
- Dow Corning 3-6891 1-PART SILICONE RUBBER ABRADABLE SEALANT COMPOUND
- BASF Ultramid® 8267G HS BK-106 15/25% Glass/Mineral Filled PA6 (Dry)
- A. Schulman POLYFLAM™ CB 3229 Medium Flow, High Impact Copolymer Polypropylene
- ExxonMobil OPPalyte® 30 HM OPP Film
Copyright © lookpolymers.com All Rights Reserved