POLYMER SEARCH

ExxonMobil Exxtral™ BMT222 Performance Polyolefin

Category	Polymer , Thermoplastic , Polyolefin
Manufacturer	Exxon Chemical
Trade Name	Exxtral™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exxtral™ BMT222 Performance Polyolefin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A specialty thermoplastic polyolefin resin characterized by good stiffness/toughness balance and designed for automotive interior applications in which good surface finish and good UV resistance are required.Availability: Africa & Middle East, Asia Pacific, Europe, North America and South America Features: Balanced Stiffness/ToughnessGood Dimensional StabilityGood Surface FinishHigh Impact ResistanceLow Temperature Impact ResistanceLow to No FoggingUses: Automotive ApplicationsAutomotive Instrument PanelAutomotive Interior PartsAutomotive Interior TrimProcessing Method: Injection MoldingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	ISO 1183
Melt Flow	6.5 g/10 min @Load 2.16 kg, Temperature 230 °C	6.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	12.0 MPa	1740 psi	ISO 527-2/50
Tensile Strength, Yield	17.4 MPa	2520 psi	ISO 527-2/50
Elongation at Break	40 %	40 %	ISO 527-2/50
Elongation at Yield	3.0 %	3.0 %	ISO 527-2/50
Tensile Modulus	1.72 GPa	249 ksi	Secant; ISO 527-2
Charpy Impact, Notched	0.546 J/cm² @Temperature -30.0 °C	2.60 ft-lb/in² @Temperature -22.0 °F	Complete Break; ISO 179
	1.49 J/cm² @Temperature 0.000 °C	7.10 ft-lb/in² @Temperature 32.0 °F	Partial Break; ISO 179
	4.20 J/cm² @Temperature 22.8 °C	20.0 ft-lb/in² @Temperature 73.0 °F	Partial Break; ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	92.2 °C	198 °F	ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	ISO 75-2/A

Users viewing this material also viewed the following: