- NatureWorks® Ingeo™ 3052D Lubricated, High Flow Biopolymer
NatureWorks® Ingeo™ 3052D Lubricated, High Flow Biopolymer
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | NatureWorks LLC |
| Trade Name | Ingeo™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NatureWorks® Ingeo™ 3052D Lubricated, High Flow Biopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NatureWorks® PLA polymer 2003D is a thermoplastic resin derived from annually renewable resources. It is designed for injection molding applications where the requirements are clarity with heat deflection temperatures below 120ºF (49ºC). Sample uses include food service products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Viscosity Measurement | 3.3 @Temperature 30.0 °C |
3.3 @Temperature 86.0 °F |
1.0 g/dl in chloroform; Relative Viscosity |
| Linear Mold Shrinkage | 0.003 - 0.005 cm/cm | 0.003 - 0.005 in/in | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 210 °C |
14 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ASTM D882 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D882 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D882 |
| Tensile Modulus | 3.72 GPa | 540 ksi | ASTM D882 |
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Flexural Modulus | 3.55 GPa | 515 ksi | ASTM D790 |
| Izod Impact, Notched | 0.1600 J/cm | 0.2997 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 - 160 °C | 293 - 320 °F | Peak; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM E2092 |
| Glass Transition Temp, Tg | 55.0 - 60.0 °C | 131 - 140 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | Thickness Unknown |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 165 °C | 329 °F | |
| Nozzle Temperature | 205 °C | 401 °F | |
| Melt Temperature | 200 °C | 392 °F | |
| Mold Temperature | 25.0 °C | 77.0 °F | |
| Moisture Content | <= 0.025 % | <= 0.025 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 100 - 175 rpm | 100 - 175 rpm |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 6900 LC BLK
- MV Labs HG700 Hg(NO3)2·xH2O Mercury(II) nitrate hydrate
- Techmer ES HiFill® HDPE LGF50 12 mm 50% Glass Filled
- Wingate Alloys Winco-Tuf 36 High Strength Wear Plate
- Elastocon TPE Technologies Elastocon® 2880L Thermoplastic Elastomer
- Azoty Tarnow™ Tarnamid® T-27 MCS V0 Polyamide 6 - Flame Retarded, Unreinforced
- Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, Conditioned
- DuPont Performance Polymers Zytel® 74G33W BK196 Nylon 66 (Unverified Data**)
- Fainplast Compounds MPH 75/D Medical Flexible PVC, Extrusion
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Thanecure® ZM
Copyright © lookpolymers.com All Rights Reserved