NOVA Chemicals Sclair® 8306 UV8D, 8306G UV8D MDPE Rotational Molding Resin (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Rotational Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 8306 UV8D, 8306G UV8D MDPE Rotational Molding Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Balanced combination of toughness, ESCR and processability.Applications: General purpose.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | >= 400 hour | >= 400 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength, Yield | 14.4 MPa | 2090 psi | ASTM D638 |
| Elongation at Break | 900 % | 900 % | ASTM D638 |
| Flexural Modulus | 0.520 GPa | 75.4 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 170 - 215 °C | 338 - 419 °F |
Users viewing this material also viewed the following:
- RheTech Products FT2600-00UV Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- Nye Lubricants NC-GP Grease
- Precision Polymer Engineering S50D Silicone Rubber
- Ferro EG 2004 Low-Temperature Sealing
- Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes
- SABIC Innovative Plastics LNP THERMOCOMP WH0270F PBT
- A. Schulman POLYBLAK™ 2076 Superior Black Color Concentrate, 40% Carbon Black Based In EVA
- BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved