- NOVA Chemicals Sclair® 19C Homopolymer HDPE Film Resin
NOVA Chemicals Sclair® 19C Homopolymer HDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 19C Homopolymer HDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Good stiffness, good barrier, high clarity, narrow MWD.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D792 |
| Water Vapor Transmission | 2.64 g/m²/day | 0.170 g/100 in²/day | ASTM F1249 |
| Oxygen Transmission Rate | 1488 cc/m²/day | 95.83 cc/100 in²/day | ASTM D3985 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.95 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 27.0 MPa | 3920 psi | ASTM D882 |
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 890 % | 890 % | ASTM D882 |
| Secant Modulus, MD | 0.840 GPa | 122 ksi | ASTM D882 |
| Secant Modulus, TD | 1.18 GPa | 171 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 0.630 g/micron | 16.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.7 g/micron | 475 g/mil | ASTM D1922 |
| Dart Drop | 1.16 g/micron | 29.5 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 131 °C | 268 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 36 % | 36 % | ASTM D1003 |
| Gloss | 23 % | 23 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP-10IM-901 Polypropylene, Mineral Filled
- Magyar Aluminum ALOLT 120F Aluminum Hydroxide
- Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C
- Solvay Specialty Polymers Ryton® R-4-222NA Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Saint-Gobain Rulon® II Bearing/Seal PTFE
- DSM Stanyl® TW250F6 Nylon 46-30% Glass Reinforced (European Grade) (Dry)
- Chosun Refractories PT-165 Plastic Refractory
- Abatron L060330-2 Flexible Polyurea Compound
- 3M Novec™ 7300 Engineered Fluid
Copyright © lookpolymers.com All Rights Reserved