- NOVA Chemicals Sclair® 11U4 Butene LLDPE Film Resin (discontinued **)
NOVA Chemicals Sclair® 11U4 Butene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 11U4 Butene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, good clarity, easy processability.Applications: Bread bags, HDPE bottle sleeves, specialty blending.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.350 cc-mm/m²-24hr-atm | 0.889 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Water Vapor Transmission | 14.0 g/m²/day | 0.902 g/100 in²/day | ASTM D1434 |
| Oxygen Transmission | 120 cc-mm/m²-24hr-atm | 305 cc-mil/100 in²-24hr-atm | or 4800 cc/m²-atm-24 hr per 25 µm film; 38°C; 90% RH Difference |
| Melt Flow | 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 16.0 MPa | 2320 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Brittleness Temperature | <= -68.0 °C | <= -90.4 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % @Thickness 0.0250 mm |
8.0 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 57 % | 57 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 230 °C | 428 - 446 °F |
Users viewing this material also viewed the following:
- Honeywell Aegisâ„¢ H100QP Nylon 6 Extrusion Grade Homopolymer Film
- SABIC Innovative Plastics LNP THERMOCOMP 5C004 FP-V (PVDF)
- Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced
- Tra-Con Tra-Bond FDA22BK01 Food and Drug Application Epoxy Adhesive
- Tra-Con Tra-Bond 2110 High Impact Epoxy Staking Compound
- Dow FLEXOMER™ ETS-9066 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin
- Biomer P226 PHB Biodegradable Polymer
- A. Schulman POLYTROPE™ TPP 504E Extrusion Grade Olefinic Thermoplastic Elastomer
- Plenco 7321 Phenolic, Nodular, Compression Molded
Copyright © lookpolymers.com All Rights Reserved