- NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin (discontinued **)
NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, strength and toughness.Applications: Co-extrusion.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.57 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.57 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 830 % | 830 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.50 | >= 0.50 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 7.00 g/micron | 178 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.0 g/micron | 406 g/mil | ASTM D1922 |
| Dart Drop | 5.00 g/micron | 127 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Brittleness Temperature | <= -90.0 °C | <= -130 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % @Thickness 0.0250 mm |
8.0 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 55 % | 55 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- MV Labs HO400 HoCl3·6H2O Holmium chloride hexahydrate
- PolyOne Gravi-Tech™ GRV-NY-085-W-NAT Polyamide 6 (Nylon 6)
- Park Electrochemical Nelcote® F-502 Phenolic Prepreg, 7781 E-Glass Reinforced
- PolyOne Geon™ Vinyl Flexible XV3715 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Iran Petrochemical (PCC) TG 641 Super Bright Polyethylene Terephthalate
- Momentive Performance Materials Metal Coated Particles
- Lucent Polymers G66-13 Nylon 66, 13% Glass Fiber Reinforced
- Fainplast Compounds FKA 92 Flexible PVC, Flame Retardant Insulation Lead Free